Sarlink® TPV X10060B
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xtSgn1_Sarlink-TPV-X10060B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Sarlink 10000 Series are TPE-V's engineered to have a low coefficient of friction against glass or painted steel specifically for automotive sealing system applications. These grades are suitable for 2K molding and exhibit excellent adhesion to polypropylene, superior UV resistance and long term performance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 5 sec, Extruded | 58 | ||
| Shore A, 5 sec, Injection Molded | 61 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.50 to 0.60 | ASTM D1894 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Across Flow : 100% Strain | 2.00 | MPa | |
| Flow : 100% Strain | 2.40 | MPa | |
| Tensile Strength | ISO 37 | ||
| Across Flow : Break | 4.40 | MPa | |
| Flow : Break | 4.40 | MPa | |
| Tensile Elongation | ISO 37 | ||
| Across Flow : Break | 370 | % | |
| Flow : Break | 300 | % | |
| Tear Strength 1 | 16 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 18 | % | |
| 70°C, 22 hr | 27 | % | |
| 125°C, 70 hr | 45 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | ISO 188 | ||
| 135°C, 1000 hr | -24 | % | |
| 100% Strain 135°C, 1000 hr | -4.0 | % | |
| 150°C, 168 hr | -23 | % | |
| 100% Strain 150°C, 168 hr | -3.0 | % | |
| Change in Tensile Strain at Break in Air - Across Flow | ISO 188 | ||
| 135°C, 1000 hr | -22 | % | |
| 150°C, 168 hr | -21 | % | |
| Change in Shore Hardness in Air | ISO 188 | ||
| Shore A, 150°C, 168 hr | 1.0 | ||
| Shore A, 150°C, 1000 hr | 0.0 | ||
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 72 | % | ISO 1817 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 180 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 205 | °C | |
| Middle Temperature | 180 to 205 | °C | |
| Front Temperature | 180 to 205 | °C | |
| Nozzle Temperature | 185 to 210 | °C | |
| Processing (Melt) Temp | 185 to 210 | °C | |
| Mold Temperature | 10.0 to 55.0 | °C | |
| Back Pressure | 0.100 to 1.00 | MPa | |
| Screw Speed | 100 to 200 | rpm |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPLEN 0024 V0 C | Vamp Tech | PP Copolymer | VAMPLEN |
| FLEXCHEM™ 7553 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |
| Hylon® N2033TL | Ravago Manufacturing Americas, LLC | Nylon 6 | Hylon® |
| SCHULABLEND® SCHULABLEND® (ABS/PA) M/MK 7102 GF20 | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |
| NORYL GTX™ GTX4610 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |