PEARLCOAT® 165K is a polyether based TPU, supplied in form of translucent, colorless pellets, combining hardness with excellent low-temperature flexibility and very good hydrolysis resistance. PEARLCOAT® 165K is used in melt coatings on textile substrates, for end-uses in industrial coatings (for life-jackets, etc.) obtained by extrusion and calendering. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, DIN 53479 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240, DIN 53505 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | DIN 53516 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, DIN 53504 | ||
| 100% strain | 7.00 | MPa | ASTM D412, DIN 53504 |
| 300% strain | 12.0 | MPa | ASTM D412, DIN 53504 |
| Tensile Strength | |||
| Yield | 30.1 | MPa | ASTM D412 |
| Yield | 30.0 | MPa | DIN 53504 |
| Tensile Elongation (Break) | 450 | % | ASTM D412, DIN 53504 |
| Tear Strength | 100 | kN/m | DIN 53515 |
| Compression Set | |||
| 23°C, 70 hr | 25 | % | ASTM D395 |
| 70°C, 24 hr | 35 | % | ASTM D395 |
| 23°C, 70 hr | 27 | % | DIN 53517 |
| 70°C, 24 hr | 50 | % | DIN 53517 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -43.0 | °C | DSC |
| Melting Temperature 1 | 162 - 172 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 149 - 160 | °C | |
| Cylinder Zone 2 Temp. | 160 - 171 | °C | |
| Cylinder Zone 3 Temp. | 168 - 179 | °C | |
| Cylinder Zone 4 Temp. | 174 - 185 | °C | |
| Die Temperature | 174 - 185 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 25:1 to 30:1Extruder Speed: 12 to 60 rpmExtruder Compression ratio: 2:1 to 3:1 |
| Note Message | |
|---|---|
| 1 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg, MQSA 111 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALFATER XL® D40E 2GP0000 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Axiall PVC 19805 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| KumhoSunny ABS 780 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Hostacom G3 N01 L303613 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| OTECH ALLOY OE8522 - Profile | OTECH Corporation | TP, Unspecified | OTECH ALLOY |