Boda BDT40EP
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xaUedU_Boda-BDT40EP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDT40EP is a medium viscosity curative incorporated fluoroelastomer terpolymer. This grade is well suited for application where good flowability, mold release and superior fluid resistance than copolymers are required. BDT40EP can be compounded to meet the major fluoroelastomer specifications. BDT40EP can be used for extrusion molding of articles, or compression molding of oil seals and complicated geometries. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.86 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 40 | MU | |
| Fluorine Content | 68 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.25 | N·m | |
| ML 2(177°C) | 0.370 | N·m | |
| t'90 3(177°C) | 3.5 | min | |
| ts2 4(177°C) | 3.5 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 75 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 13.0 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 260 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 26 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BS70OR6594 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| BP Flex D 4107 GO1 BLK | Buckeye Polymers, Inc. | TPO | BP Flex |
| Hytrel® G4078LS NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| Karina WHITE COLOR CONCENTRATE -E 10/ 77-GE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Complet® LCF10-LGF20-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |