Pinnacle PP 1350N
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Pinnacle Polymers |
| Trademark: | Pinnacle PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 29clVz_Pinnacle-PP-1350N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
55 MELT FLOW HOMOPOLYMER POLYPROPYLENE FOR INJECTION MOLDING Pinnacle Polymers Polypropylene 1350N is made via UNIPOL™ PP technology, which utilizes gas-phase fluidized bed reactors with a high activity catalyst system to ensure uniform physical properties and lot-to-lot consistency. This product is intended for general-purpose injection molding of thin wall containers. 1350N contains a nucleation additive package. The 1350N product provides:
Pinnacle's polypropylene, as marketed by Pinnacle Polymers, in natural, uncolored pellet form complies with appropriate requirements of CFR Title 21, Part 177, Subpart B, Section 177.1520 (c) 1.1a entitled "Olefin Polymers" of the Food Additives Amendment of 1958 to the United States Food, Drug and Cosmetic Act of 1938. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 55 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm, Injection Molded) | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, 3.20 mm, Injection Molded) | 8.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(3.20 mm, Injection Molded) | 2000 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 4(23°C, 3.20 mm, Injection Molded) | 27 | J/m | ASTM D256 |
| Notched Izod Impact (Area) 5(23°C, 3.20 mm, Injection Molded) | 2.60 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 116 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | Type I, 1.3 mm/min |
| 4 . | Type I |
| 5 . | Type I |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-2095-40A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Sylvin 5137-94 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Moplen HP400M | LyondellBasell Industries | PP, Unspecified | Moplen |
| Karina CLEAR PVC COMPOUND -E 70850/200-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Comco PA6G OL | Comco Nylon GmbH | Nylon 6 | Comco |