SILVER® PE 1044.GH
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Guangdong Silver Age Sci & Tech. Co., Ltd |
| Trademark: | SILVER® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pRqzcK_SILVER-PE-1044-GH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SlLVER® Modified Polyolefin includes modified polyethylene and modified polypropylene. Modified polyethylene is mainly applied to cable jacket. Black polyethylene compound is composed of polyethylene resin,carbon black, antioxidantand so on. Black polyehylene compound is applied to communication cable,contoll cable,signal cable,power cable,opticalcable and submarine cable. It conforms to GB15065-94 Standard. Modified PP including flame resistant, glass fiber andmineral reinforced and weather—resistant, is widely applied in electronic & electrical appliances, household appliances, autoaccessories, lightings, mechanical components and sockets, and so on. In addition, we develop new products according to customer's specific requirements. Characteristics:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 0.928 to 0.958 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | < 0.50 | g/10 min | |
| Environmental Stress-Cracking Resistance (F0) | > 500 | hr | |
| Carbon Black Content | 2.4 to 2.9 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 22.0:1.0 to 26.0:1.0 |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength | |||
| Yield | > 16.0 | MPa | |
| -- | > 20.0 | MPa | |
| Tensile Elongation | |||
| Break 1 | > 180 | % | |
| Break 2 | > 650 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | |
| Vicat Softening Temperature | > 110 | °C |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Volume Resistivity | > 1.0E+6 | ohms·cm | |
| Dielectric Strength | > 25 | kV/mm | |
| Dielectric Constant (1 MHz) | < 2.75 | ||
| Dissipation Factor | < 5.0E-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 195 | °C | |
| Cylinder Zone 3 Temp. | 195 to 200 | °C | |
| Cylinder Zone 5 Temp. | 200 to 205 | °C | |
| Die Temperature | 205 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | under low temperature |
| 2 . | 100 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ELASTOSIL® R 780/80 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| EPLAMID 66 MOS2 %2 GFR 40 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| ESTOPLAST EP 4730WW01 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| Polygen SC75C | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |
| LNP™ THERMOCOMP™ UF006S compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |