LNP™ STAT-KON™ OX92182 compound
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mfYEwp_LNP-STAT-KON-OX92182-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON OX92182 is a compound based on PPS-Branched resin containing Glass Fiber, Carbon Fiber, Mineral. Added features include : Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-O-92182 Product reorder name: OX92182 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.62 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (24 hr) | 0.10 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 145 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 16500 | MPa | ISO 178 |
| Flexural Stress | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 15 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 250 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.5E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 4.6E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-8431 | Teknor Apex Company | TPE | Telcar® |
| Dow ENDURANCE™ HFDK-4201 SCsb | The Dow Chemical Company | LDPE | Dow ENDURANCE™ |
| Karina MBU LILAC E 34/160-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polimid A 25 GF V0F K | Poliblend S.p.a. | Nylon 66 | Polimid A |
| Sylvin 8323-90 Grey 9323 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |