TES J-1200/30
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | TES |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fxUH3B_TES-J-1200-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Molding Parameters: For 2-zone machines, the rear temperature is 450-520°F, and the front temperature is 420-470°F. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.20 | % | |
| 6.35 mm | 0.30 | % | |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6890 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 89.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6890 | MPa | ASTM D790 |
| Flexural Strength (Break, 23°C) | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 110 | °C | |
| 1.8 MPa, Unannealed | 102 | °C | |
| RTI Elec | UL 746 | ||
| 1.47 mm | 60.0 | °C | |
| 3.05 mm | 60.0 | °C | |
| 6.10 mm | 60.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.47 mm | 60.0 | °C | |
| 3.05 mm | 60.0 | °C | |
| 6.10 mm | 60.0 | °C | |
| RTI Str | UL 746 | ||
| 1.47 mm | 60.0 | °C | |
| 3.05 mm | 60.0 | °C | |
| 6.10 mm | 60.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | HB | ||
| 3.05 mm | HB | ||
| 6.10 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 216 to 232 | °C | |
| Middle Temperature | 221 to 238 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Nozzle Temperature | 199 to 221 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4702-00 | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Adell PP EH-16 | Adell Plastics, Inc. | PP, Unspecified | Adell PP |
| INSULCAST® 116 FR-FC | ITW Polymers Coatings North America | Epoxy | INSULCAST® |
| Jampilen HP500M | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Sylvin 4200-75UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |