Integra™ POK 9060
| Category: | PK , Polyketone |
| Manufacturer: | PolySource, LLC |
| Trademark: | Integra™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M3FAFz_IntegraPOK9060.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyketone, Aliphatic, High viscosity grade for injection molding & extrusion, Natural |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (240°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.8 - 2.0 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60%RH) | 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 60.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 300 | % | ASTM D638 |
| Flexural Modulus | 1570 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 60.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 177 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 105 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Iupiace® LN23 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| LEXAN™ 241S resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| LUVOCOM® 1-3260/schwarz | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Estane® ZHF90AT2 NAT 055 | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Durethan® AKV 30 G H2.0 SR1 900051 | LANXESS GmbH | Nylon 66 | Durethan® |