XIRAN® SG260
| Category: | SMA , Styrene Maleic Anhydride |
| Manufacturer: | Polyscope Polymers BV |
| Trademark: | XIRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yP9mgB_XIRAN-SG260.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
XIRAN® SG260 are SMA (styrene maleic anhydride) based injection molding compounds with:
Application areas XIRAN® SG260 is a 30% glass filled injection molding compound designed for applications with high stiffness-strength. These products are very suitable for painted and foamed parts, high temperature resistance and precision parts with high shot to shot consistency. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 2.5 | g/10 min | ISO 1133 |
| Spiral Flow 1 | 26.0 | cm | Internal Method |
| Molding Shrinkage 2 | Internal Method | ||
| Across Flow | 0.50 | % | |
| Flow | 0.20 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 34 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 8.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 120 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 118 | °C | ISO 306/B |
| CLTE | ASTM D696 | ||
| Flow : -30 to 80°C | 2.9E-5 | cm/cm/°C | |
| Transverse : -30 to 80°C | 4.7E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Processing (Melt) Temp | < 285 | °C |
| Note Message | |
|---|---|
| 1 . | 2 mm |
| 2 . | Measured according to the Autodesk Mold flow Plastics Labs using a tag mold. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Phenolic FM 4005X4649 | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| 3M™ Dyneon™ PTFE Compound TF 3105 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Di-Pak™ R-4528/30 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| HIPLEX® TR-455 natural | HIP-PetroHemija | HDPE | HIPLEX® |
| KOPLA PA6 KNG1030F | KOPLA Co., Ltd. | Nylon 6 | KOPLA PA6 |