Mineralblend® PP-2400
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | Mineralblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dgxMun_Mineralblend-PP-2400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineralblend® PP-2400 is a medium flowmica filled polypropylene homopolymer compound characterized by good stiffness and dimensional stability with additional low shrink age properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.90 to 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 2750 | MPa | ASTM D790 |
| Flexural Strength | 57.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 4.00 mm | 130 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm | 80.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 190 to 200 | °C | |
| Front Temperature | 200 to 210 | °C | |
| Nozzle Temperature | 210 to 220 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 60.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9875H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Tarflen® SM-B60 | Grupa Azoty S.A. | PTFE | Tarflen® |
| Wondel® C CSAH | Nanjing Julong Engineering Plastics Co., LTD | PC+ABS | Wondel® C |
| Nypol® PA B3 HF NTLA010 NT324 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| LEXAN™ FXM121R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |