LNP™ STAT-KON™ RE0039 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EBGgzK_LNP-STAT-KON-RE0039-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* RE0039 is a compound based on Nylon 66 resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant. Also known as: LNP* STAT-KON* Compound RC-1003 FR Product reorder name: RE0039 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.68 to 0.78 | % | ISO 294-4 |
| Flow : 24 hr | 0.17 to 0.26 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.55 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.87 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17600 | MPa | ASTM D638 |
| -- | 15600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 206 | MPa | ASTM D638 |
| Break | 210 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 11400 | MPa | ASTM D790 |
| -- | 14200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 298 | MPa | ASTM D790 |
| -- | 319 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C 2 | 8.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D4812 |
| 23°C 3 | 46 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.10 | J | ASTM D3763 |
| -- | 2.35 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 248 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 228 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.6E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V964A | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Shandong PA1010 PA1010 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 1010 | Shandong PA1010 |
| EXPLORE® CT PP | Matrix Polymers | PP, Unspecified | EXPLORE® |
| Infino GW-1010 | SAMSUNG SDI CO., LTD. | PC | Infino |
| Plexiglas® V825-UVA5A | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |