LNP™ LUBRICOMP™ NL001 compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cvcY0I_LNP-LUBRICOMP-NL001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* NL001 is a compound b ased on PC+ABS resin containing 5% PTFE. Added features include: Wear Resistant, Suitable for Thin Wall Applications. Also known as: LNP* LUBRICOMP* Compound PCA-L-4010 Product Reorder name: NL001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.14 | g/cm³ | ASTM D792 |
| -- | 1.10 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 26.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2410 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 53.1 | MPa | ASTM D638 |
| Yield | 45.0 | MPa | ISO 527-2/5 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Break 3 | 42.7 | MPa | ASTM D638 |
| Break | 40.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.6 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/5, ISO 527-2/50 |
| Break 5 | 24 | % | ASTM D638 |
| Break | 45 | % | ISO 527-2/5 |
| Break | 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2440 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 86.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| -30°C 10 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 10 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 42.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 116 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 114 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 98.9 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 100 mm Span 13 | 95.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 113 | °C | ISO 306/B50 |
| -- | 115 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 7.0E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 8.7E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 21 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 232 to 243 | °C | |
| Middle Temperature | 249 to 260 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 249 to 271 | °C | |
| Mold Temperature | 37.8 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SCP-300A70 | SHIN-A T&C | Epoxy | SHIN-A |
| Tenite™ Propionate 358A4000018 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Hostacom X M2 T28 | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| INNOPOL® PP CS 4-8000 | Inno-Comp Ltd. | PP Random Copolymer | INNOPOL® PP |
| Sylvin 7403-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |