Order Products : sales@su-jiao.com
LNP™ LUBRICOMP™ ZL003 compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RtBaO4_LNPLUBRICOMPZL003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP ZL003 is a compound based on PPE+PS Blend resin containing PTFE. Added features include Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound ZL-4030 Product reorder name: ZL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.89 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 49.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Flexural Stress | 81.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 140 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 123 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 8.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 277 - 288 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 299 - 310 | °C | |
| Processing (Melt) Temp | 299 - 304 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3489 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Mirakutoran® TPU E680 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Sindustris POM HI516W | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| Hanwha Total PP RP100E140 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Karina CLEAR PVC COMPOUND 76/201-D-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |