SABIC® PP PHC27
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZSon1M_SABIC-PP-PHC27.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This grade combines very high impact resistance, also at low temperatures, with a good stiffness and offers very good flow properties. Due to its narrow molecular weight distribution and very low tendency to warp, it is highly suitable for injection moulding of crates & boxes, suitcase shells and automotive parts. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 | |
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1050 | MPa | ASTM D638 |
| -- | 1000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 21.0 | MPa | ASTM D638 |
| Yield | 21.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 8.0 | kJ/m² | |
| 0°C | 15 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -20°C | 100 | J/m | ASTM D256A |
| 0°C | 180 | J/m | ASTM D256A |
| 23°C | No Break | ASTM D256A, ISO 180/1A | |
| -20°C | 9.0 | kJ/m² | ISO 180/1A |
| 0°C | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 80.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 50.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 145 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 65.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ PTFE Compound TF 4215 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Gallonprene® GP420-3503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Elastollan® 1174D | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Hybrid B3030U | Ravago Manufacturing Americas, LLC | PC+PBT | Hybrid |
| RTP 199 X 125315 | RTP Company | PP, Unspecified | RTP |