NORYL GTX™ EXNX0080 resin
| Category: | PPS+PPE , Polyphenylene Sulfide + PPE |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZObXB6_NORYLGTXEXNX0080resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL APS* EXNX0080 resin is a glass filled, high performance blend of PPE/PPS that exhibits an excellent balance of high-heat resistance, strength, flame retardant, and conductivity. This grade can be electro-statically painted or powder coated without the need for a conductive primer. The resin is injection moldable and only available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.020 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 16300 | MPa | ASTM D638 |
| -- | 15000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 79.2 | MPa | ASTM D638 |
| Yield | 89.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 79.2 | MPa | ASTM D638 |
| Fracture | 89.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 0.64 | % | ASTM D638 |
| Yield | 0.64 | % | ISO 527-2/5 |
| Fracture 5 | 0.66 | % | ASTM D638 |
| Fracture | 0.66 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 12700 | MPa | ASTM D790 |
| -- 7 | 13600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 0.980 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 35 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 37 | J/m | ASTM D256 |
| 23°C | 34 | J/m | ASTM D256 |
| -30°C 10 | 34 | kJ/m² | ISO 180/1A |
| 23°C 11 | 34 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 3.60 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 234 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 12 | 229 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 231 | °C | ASTM D1525, ISO 306/B120 10 13 |
| -- | 233 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.5E+4 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® C015EG | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| Sarlink® TPV 2664 | Teknor Apex Company | TPV | Sarlink® TPV |
| ULTEM™ AUT210 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Elastollan® 1147 D FHF | BASF Polyurethanes GmbH | TPU-Polyether | Elastollan® |
| Karina IVORY PVC COMPOUND 105909-35/ 1-DY-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |