Staramide AG4K
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RLtkAp_Staramide-AG4K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide AG4K is a Heat and Hydrolytically Stabilized, 20 % Glass Fiber Reinforced Polyamide 66 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.50 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 5.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 6800 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3(23°C) | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -40°C | 4.0 | kJ/m² | |
| -20°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 245 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 230 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 255 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.1E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 9.5E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.33 | W/m/K | ISO 8302 |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 6 | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 19 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.40 | ||
| 60 Hz | 3.40 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 6.8E-3 | ||
| 60 Hz | 6.8E-3 | ||
| 1 MHz | 0.015 | ||
| Comparative Tracking Index | IEC 60112 | ||
| -- | 500 | V | |
| Solution B | 400 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | FMVSS 302 | ||
| 2.00 mm | 10 | mm/min | |
| 3.00 mm | 5.0 | mm/min | |
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 |
| 6 . | ROA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TB120IR | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| SUPREME GPPS SC203EL | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| HIFOR Xtreme® SC74844 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |
| LNP™ THERMOCOMP™ RZ0069 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| LNP™ STAT-KON™ 9X02785 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |