INEOS PP N01G-02
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FNoQdH_INEOS-PP-N01G-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| N01G-02 is a low melt flow rate polypropylene impact copolymer designed for blow molding, extrusion, and compounding applications. The grade benefits from a very high impact resistance at room and low temperatures and a general purpose additive package. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 25.6 | MPa | |
| Break | 16.3 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 8.2 | % | |
| Break | 290 | % | |
| Flexural Modulus - 1% Secant | 1200 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (-20°C) | 85 | J/m | ASTM D256 |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 8.70 | kJ/m² | |
| 23°C | No Break | ||
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Ductile | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 91.7 | °C | |
| 1.8 MPa, Unannealed | 50.6 | °C | |
| Vicat Softening Temperature | 151 | °C | ASTM D1525 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 59 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2100 AR 15 TFE 10 | RTP Company | PEI | RTP |
| Genestar™ G1302 | Kuraray Co., Ltd. | Nylon 9T | Genestar™ |
| Escorene™ Ultra LD 705.MJ Molding | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Hifax TKC 461X 1 Black | LyondellBasell Industries | PP Alloy | Hifax |
| LNP™ LUBRICOMP™ OCP34E compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |