PRL PC-G30
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | sKQpeQ_PRL-PC-G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC-G30 is a Polycarbonate (PC) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.0 to 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 124 | MPa | |
| Break, 3.18 mm | 124 | MPa | |
| Flexural Modulus (3.18 mm) | 6890 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 152 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 146 | °C | |
| RTI Elec | UL 746 | ||
| 1.70 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.70 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C | |
| RTI Str | UL 746 | ||
| 1.70 mm | 80.0 | °C | |
| 3.00 mm | 80.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.70 mm | V-2 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 to 124 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Processing (Melt) Temp | 302 to 329 | °C | |
| Mold Temperature | 82.2 to 116 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAMAT EP5001C(f1) | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | SAMAT |
| AIE PA6 50G3ST | Asia International Enterprise (Hong Kong) Limited | Nylon 6 | AIE PA6 |
| ALCOM® POM 770/1 GF20 PTFE15 | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALCOM® POM |
| CP PRYME庐 Polypropylene PPC100NB-12M | Chase Plastics Services Inc. | PP Copolymer | CP PRYME® Polypropylene |
| Karina BLUE PVC COMP. -E 851-06/347-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |