Fibremod™ GB477HP
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cgocgc_Fibremod-GB477HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod GB477HP is a 40 % chemically coupled high performance glass fibre reinforced polypropylene compound intended for injection moulding. The product is available in standard black 9502. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.7 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Vertical flow direction : 2.00mm | 0.70 - 1.1 | % | Internal method |
| Flow direction : 2.00mm | 0.10 - 0.30 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 10000 | MPa | ISO 527-2 |
| Tensile Stress | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.8 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 9000 | MPa | ISO 178 |
| Flexural Stress | 175 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 11 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 59 | kJ/m² | ISO 179/1eU |
| 23°C | 62 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 153 | °C | ISO 75-2/A |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | Internal method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | µgC/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 70.0 | °C | |
| Holding Pressure | 30.0 - 70.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 150x80x2 |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide BR-17 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| FRblend® PBT-1500 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | FRblend® |
| Formolene® 6510E | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Ecotan B FL HI 1 SB NAT | Soredi S.p.a. | Nylon 6 | Ecotan B |
| Jampilen HP524J | Jam Polypropylene Company | PP Homopolymer | Jampilen |