Elastollan® 590 A
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | usKgxd_Elastollan-590-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and in particular, good abrasion resistance. Typical applications Shoes, parts subject to regular wear and tear, castor tyres and films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 7619 | ||
| Shore A, 3 sec | 94 | ||
| Shore D, 3 sec | 41 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 35.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 50.0 | MPa | DIN 53504 |
| Tensile Elongation (Break) | 600 | % | DIN 53504 |
| Tear Strength 1 | 100 | kN/m | ISO 34-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 175 to 230 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 175 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | Method Bb, Angle (Nicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULATEC® PEEK GF 30 NV 12 | A. Schulman Europe | PEEK | SCHULATEC® |
| Suprel® SVA 9301 | Axiall Corporation | PVC, Rigid | Suprel® SVA |
| Unichem 6533 | Colorite Polymers | PVC, Unspecified | Unichem |
| DuraStar™ MN621 | Eastman Chemical Company | Polyester, TP | DuraStar™ |
| MAJORIS FFRH260R | AD majoris | PP, Unspecified | MAJORIS |