TECHNO MUH BM5614

Category:	ABS , Acrylonitrile Butadiene Styrene
Manufacturer:	Techno Polymer America, Inc.
Trademark:	TECHNO MUH
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	XpbHhT_TECHNO-MUH-BM5614.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

A better replacement for modified PPE used in the air spoiler parts of automobiles

An optimum balance of impact strength and heat deflection temperature for air spoilers

Uniform wall thickness and parts weight for fewer parison sag problems

Fewer black particles and pits problems for reduced defects in the blow-molding process and shorter sanding time

Lower cylinder temperature than modified PPE for quicker recovery time after a machine goes down.

Lower throughput cost for blow-molding producers

The best material for air spoiler parts that require a higher aesthetic appearance and lower cost

General Information
Features	Good Dimensional Stability Good Impact Resistance Medium Heat Resistance
Uses	Automotive Under the Hood
Forms	Pellets
Processing Method	Blow Molding

Physical	Nominal Value	Unit	Test Method
Density	1.05	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR)			ISO 1133
220°C/10.0 kg	1.2	g/10 min
240°C/10.0 kg	2.8	g/10 min

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	48.0	MPa	ISO 527-2
Tensile Elongation (Break)	18	%	ASTM D638
Flexural Modulus	2200	MPa	ISO 178
Flexural Stress	71.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179
-30°C	7.0	kJ/m²
23°C	19	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	93.0	°C	ISO 75-2/B

Additional Information	Nominal Value	Unit
Blow Molding Barrel Temperature	220 to 225	°C
Blow Molding Melt Temperature	235	°C
Blow Molding Mold Temperature	71	°C
Drying Temperature - Blow Molding	93 to 102	°C
Drying Time - Blow Molding	3.0 to 5.0	hr

Resin Grade	Manufacturer	Category	Trademark
SABIC® PP 526K	Saudi Basic Industries Corporation (SABIC)	PP Homopolymer	SABIC® PP
Adiprene® LF 930A	Chemtura	PUR-Ether/TDI	Adiprene®
Flontech® FT-PK20-GR5-1	Guarniflon S.p.A. - Flontech Division	PEEK+PTFE	Flontech®
Elastollan® 560 D	BASF Polyurethanes GmbH	TPU-Polyester	Elastollan®
Karina BLACK PVC COMPOUND E-CAK 60-48/1	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina