Generic Acetal (POM) Copolymer - Aramid Fiber
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4tEKov_Generic-Acetal-POM-Copolymer---Aramid-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - Aramid Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 - 1.52 | g/cm³ | ASTM D792 |
| 23°C | 1.40 - 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 1.1 - 3.0 | % | ASTM D955 |
| 23°C | 1.5 - 1.8 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2760 - 4190 | MPa | ASTM D638 |
| 23°C | 2200 - 3510 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Fracture, 23°C | 39.0 - 60.9 | MPa | ISO 527-2 |
| 23°C | 52.3 - 62.1 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 6.4 - 10 | % | ASTM D638 |
| Yield, 23°C | 2.9 - 8.8 | % | ISO 527-2 |
| Fracture, 23°C | 4.0 - 14 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2600 - 3590 | MPa | ASTM D790 |
| 23°C | 2000 - 3130 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 68.5 - 97.1 | MPa | ASTM D790 |
| 23°C | 60.0 - 75.0 | MPa | ISO 178 |
| Coefficient of Friction | 0.055 - 0.23 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.5 - 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 25 - 50 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 58 - 80 | J/m | ASTM D256 |
| 23°C | 5.0 - 8.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 370 - 590 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 120 - 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 84.0 - 135 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 121 | °C | |
| Drying Time | 1.9 - 5.0 | hr | |
| Rear Temperature | 182 - 194 | °C | |
| Middle Temperature | 193 - 199 | °C | |
| Front Temperature | 190 - 216 | °C | |
| Processing (Melt) Temp | 200 - 208 | °C | |
| Mold Temperature | 93.0 - 100 | °C | |
| Injection Pressure | 86.0 - 86.2 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Acetal (POM) Copolymer - Aramid FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AW33 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| Nylene® 7140 HS | Custom Resins Group | Nylon 66 | Nylene® |
| Geon™ Vinyl Flexible 90013 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hostalen GC 7260 | LyondellBasell Industries | HDPE | Hostalen |
| LubriOne™ PC-10CF/15T BLACK | PolyOne Corporation | PC | LubriOne™ |