InnoFR™ FX-8575
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoFR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4AkbDl_InnoFR-FX-8575.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FX-8575 is a rigid polyurethane formulated hand casting methods. Excellent physical properties can be obtained with a mild post cure without the utilization of mercury, MOCA, or TDI. This material passes UL 94VO. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.10 | g/cm³ | |
| Cured | 1.23 | g/cm³ | |
| Base Resin | 1.26 | g/cm³ | |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1930 | MPa | ASTM D790 |
| Flexural Strength | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 50.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 72 Mix Ratio by Weight: 63 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time (66°C) | 60 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Exotherm - 200g mass | 138 | °C |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.060 | Pa·s | |
| 25°C 2 | 0.18 | Pa·s | |
| 25°C 3 | 0.88 | Pa·s | |
| Curing Time 4 | 25 | hr | |
| Gel Time | 10 to 15 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 77 to 87 | ASTM D2240 | |
| Tensile Modulus | 2280 | MPa | |
| Tensile Strength | 77.2 | MPa | ASTM D638 |
| Tensile Elongation at Break | 6.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 1 hour at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-9610 | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| Borealis FR4832 | Borealis AG | XLPE | Borealis |
| Gallonprene® GP550-7503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Elastane™ 4762-82A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Kepital® FW-24 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |