Baytec® GS-V85A (82A)
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kCuXO0_Baytec-GS-V85A-82A-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec GS-V85A is a two-component, one-shot system that yields a solid polyurethane elastomer. The isocyanate component is an isocyanate-terminated (MDI) polyester prepolymer, and the polyol component is a polyethylene/polybutylene adipate diol. The Baytec GS-V85A system is used in the production of cast polyurethane elastomers. As with any product, use of the Baytec GS-V85A system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 82 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 39.9 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 480 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 56.0 | kN/m | ASTM D624 |
| Cracking | 12 | kN/m | ASTM D1938 |
| Compression Set (70°C, 22 hr) | 20 | % | ASTM D395B |
| Bayshore Resilience | 51 | % | ASTM D2632 |
| Thermoset | Nominal Value | ||
|---|---|---|---|
| Thermoset Components | |||
| Part C 2 | Mixing ratio by weight: 7.5 | ||
| Component a 3 | Mixing ratio by weight: 60 | ||
| Component B 4 | Mixing ratio by weight: 93 |
| Additional Information |
|---|
| Part A Type: Isocyanate Appearance: Pale yellow liquid Specific Gravity @ 25°C: 1.20 Viscosity @25°C: 1100 mPa Flash Point, PMCC: 207°C NCO: 18.9 wt% Bulk Density at 25°C: 10.01 lb/gal Part B Type: Polyol Appearance: Light yellow liquid Specific Gravity @ 25°C: 1.17 Viscosity @25°C: Semisolid Flash Point, PMCC: 216°C Bulk Density at 25°C: 9.76 lb/gal Hydroxyl Number: 55 mg KOH/g Material Temperature: 55 to 60°CMold Temperature: 110°CDemold Time: 0.5 to 4 hr |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 1,4 Butone Diol |
| 3 . | Isocyanate |
| 4 . | Polyol |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 EC2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| TPV Elastoprene® N55A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Ultralast™ PE541 | Chemtura | PUR-Ether/PPDI | Ultralast™ |
| Fainplast PVC GK 75 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Petrothene® XL07425 | LyondellBasell Industries | Polyolefin, Unspecified | Petrothene® |