UmaPET IT

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Ester Industries Ltd.
Trademark:	UmaPET
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ziHwX9_UmaPET-IT.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

KEY FEATURES

Uma PET IT is transparent film with plain surfaces in both sides. One side chemically coated or corona treated is also available as option.

This film shows excellent isotropic characteristics i.e. high and balanced mechanical properties alongwith good thermal, mechanical, optical and surface properties.

APPLICATIONS

The film is widely used for lidding, printing, coating applications as well as lamination with paper and thin foils, metallising applications.

General Information
Features	Excellent Printability Good Surface Finish Metallizable Opticals
Uses	Coating Applications Film Foil Coatings Laminates Lids
Appearance	Clear/Transparent
Forms	Film

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage			ASTM D1204
Flow : 150°C, 30 min, 0.0120 mm	2.2	%
Flow : 150°C, 30 min, 0.0230 mm	2.2	%
Across Flow : 150°C, 30 min, 0.0120 mm	0.0	%
Across Flow : 150°C, 30 min, 0.0230 mm	0.0	%

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction			ASTM D1894
vs. Itself - Dynamic ¹	0.45
vs. Itself - Dynamic ²	0.42
vs. Itself - Static ³	0.50
vs. Itself - Static ⁴	0.48

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	12 23	µm
Film Thickness - Recommended / Available	12, 23 µm
Tensile Strength			ASTM D882
MD : Break, 12 µm	216	MPa
MD : Break, 23 µm	196	MPa
TD : Break, 12 µm	226	MPa
TD : Break, 23 µm	206	MPa
Tensile Elongation			ASTM D882
MD : Break, 12 µm	100	%
MD : Break, 23 µm	100	%
TD : Break, 12 µm	95	%
TD : Break, 23 µm	95	%
Yield			Internal Method
12.0 µm	59.5	m²/kg
23.0 µm	31.0	m²/kg

Additional Information	Nominal Value	Unit	Test Method
Wetting Tension - Plain side			ASTM D2578
12.0 µm	44	dyne/cm
23.0 µm	44	dyne/cm

Optical	Nominal Value	Unit	Test Method
Haze			ASTM D1003
12.0 µm	3.5	%
23.0 µm	4.5	%

Note Message
1 .	12 µm
2 .	23 µm
3 .	12 µm
4 .	23 µm

Resin Grade	Manufacturer	Category	Trademark
MIRASON™ 500BK1	Mitsui Chemicals, Inc.	LDPE	MIRASON™
MonoSol® MC-1257	MonoSol, LLC	MHPC	MonoSol®
XYRON™ X8610	Asahi Kasei Chemicals Corporation	PPE+PS	XYRON™
Elastron® V V601.A70.N	Elastron USA, Inc.	TPV	Elastron® V
KEP® 2320	Kumho Polychem Co., Ltd.	EPDM	KEP®