LNP™ LUBRICOMP™ IFP36 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zfbm8W_LNP-LUBRICOMP-IFP36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP IFP36 is a Nylon 6/12 base resin containing 30% Glass Fiber, 15% PTFE/Silicone. Added features of t his grade include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound IFL-4536 Product reorder name: IFP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.45 | g/cm³ | ASTM D792 |
| -- | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.19 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.28 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 9700 | MPa | ASTM D638 |
| -- | 9730 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 145 | MPa | ASTM D638 |
| Yield | 146 | MPa | ISO 527-2/5 |
| Break 3 | 145 | MPa | ASTM D638 |
| Break | 146 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.8 | % | ASTM D638 |
| Yield | 2.7 | % | ISO 527-2/5 |
| Break 5 | 2.8 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 8870 | MPa | ASTM D790 |
| -- 7 | 8950 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 225 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 229 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 229 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.62 | ||
| vs. Itself - Static | 0.52 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 1.90 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 10 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 11 | 60 | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | 2.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 214 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 214 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 200 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 197 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 1.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRAN® WLFT 511BL | SAMBARK | TP, Unspecified | SUPRAN® |
| TAROMID B 280 Z3 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| Trilene® HI35HO | Chandra Asri Petrochemical | PP Homopolymer | Trilene® |
| NITRICLEAN 3350 X | NITRIFLEX | NBR | NITRICLEAN |
| Elastollan® 1195A10 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |