Order Products : sales@su-jiao.com
RTP 4000 AT-1001 L
| Category: | PPA , Polyphthalamide |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 7T0ir9_RTP-4000-AT-1001-L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact Modified - Lubricated |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.6 | % | ASTM D955 |
| Moisture Content | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2070 | MPa | ASTM D638 |
| Tensile Strength | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 79.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 960 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 110 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 107 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 304 - 332 | °C | |
| Mold Temperature | 93.3 - 138 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Derakane® 411-45 | Ashland Performance Materials | Vinyl Ester | Derakane® |
| KOPA® KN135HB30HIBL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Latene® AG7H G/30 | LATI S.p.A. | PP Homopolymer | Latene® |
| Lucky Enpla LAY1001F | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |
| Petro Rabigh PE M8060 | Rabigh Refining & Petrochemical Co. | HDPE | Petro Rabigh PE |