Durethan® AM 40 X H2.0 DUS041 901510
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zRSTro_DurethanAM40XH20DUS041901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 40 % glass fibers/mineral, injection molding, heat-aging stabilized, low tendency to warp |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.46 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 290°C, 2.00mm 1 | 1.0 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.10 | -- | % | ISO 2577 |
| Flow direction : 290°C, 2.00mm 3 | 0.45 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.050 | -- | % | ISO 2577 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10600 | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 150 | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.7 | 5.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 9700 | 6000 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | -- | 140 | MPa | ISO 178/A |
| 23°C 6 | 240 | 150 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.0 | 5.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHR, 14-120, (GF+MD) 40 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 55 | 60 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 10 | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 45 | 45 | kJ/m² | ISO 180/1U |
| 23°C | 50 | 55 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 230 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 260 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V191A NAT601 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Tarflen® SM-K25 | Grupa Azoty S.A. | PTFE | Tarflen® |
| Celstran® TPU-GF60-01 | Celanese Corporation | TPU, Unspecified | Celstran® |
| COSMOTHENE® G215 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® |
| Dryflex® A2 600509 | ELASTO | SEBS | Dryflex® |