LNP™ THERMOCOMP™ PFB91S compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 75fKGm_LNP-THERMOCOMP-PFB91S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP PFB91S is a compound based on Nylon 6 resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-P-00461 Product reorder name: PFB91S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7490 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Break | 62.1 | MPa | |
| Break 2 | 62.1 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break | 2.7 | % | |
| Break 3 | 2.7 | % | |
| Flexural Modulus | ASTM D790 | ||
| -- | 6050 | MPa | |
| 50.0 mm Span 4 | 6050 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 280 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 163 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L AB305 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| TEREZ PA 6.6 7510 GF 25 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| VITAMIDE® BW36 | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| APEX® 85-J438D-6 | Teknor Apex Company | PVC, Flexible | APEX® |
| Cheng Yu N66C1 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |