E 5201 is a broad molecular weight distribution HDPE, produced by the Mitsui CX Process. This resin is particularly recommended for high ESCR Blow Molding, Cable Sheathing & Jacketing Compound, Lamination Film, General Purpose Film and Extrusion Applications. E 5201 combines exceptional processability with high ESCR and excellent mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, Compression Molded, F50) | > 600 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield, molding | 23.0 | MPa | ASTM D638 |
| Fracture, molding | 34.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | > 1000 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 950 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 140 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 78.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 4 |
| Peak Melting Temperature | 130 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 160 | °C | |
| Die Temperature | 160 - 165 | °C |
| Extrusion instructions |
|---|
| Parison Temperature: 160-170°CCooling Water for Mold: 20-25°C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 HI/1 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Ultrason® S 3010 MR UN | BASF Corporation | PSU | Ultrason® S |
| Geon™ Vinyl Wire & Cable WJMS800 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| KOCETAL® K200BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Sylvin 5175-92 Green 3145 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |