Trilene® HF8.0CM
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Chandra Asri Petrochemical |
| Trademark: | Trilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xruqZb_Trilene-HF8-0CM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trilene HF8.0CM is a polypropylene homopolymer for production of cast film, including film to be metallized. This grade uses Unipol® polypropylene technology with the latest catalyst technology. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.903 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1280 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 30 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 104 | °C | ASTM D648 |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 3 |
| Peak Melting Temperature 4 | 163 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 to 260 | °C | |
| Take-Off Roll | 30.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | Rate B (120°C/h) |
| 4 . | 10°C/min, 2nd heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol HT121E | LyondellBasell Industries | PP Copolymer | Supol |
| Tarnamid® T- 27 GF10 MX10 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Vydyne® R533H BK0201 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| APEX® CXFR 2001-84 | Teknor Apex Company | PVC, Flexible | APEX® |
| Cevian®-PC 5100 | PlastxWorld Inc. | PC | Cevian®-PC |