Zytel® 80G33HS1L NC010
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | zFIn5a_Zytel-80G33HS1L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 33% Glass Reinforced, Toughened, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.70 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ||||
| 24 hr | 0.85 | -- | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 4.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.5 | -- | % | ISO 62 |
| Viscosity Number | 160 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale | 70 | -- | ||
| R-Scale | 110 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8900 | 6200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 146 | 108 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.7 | 7.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 5300 | MPa | |
| 1000 hr | -- | 4300 | MPa | |
| Flexural Modulus | 7500 | 6200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 14 | 18 | kJ/m² | |
| -30°C | 18 | 17 | kJ/m² | |
| 23°C | 20 | 28 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 110 | 100 | kJ/m² | |
| 23°C | 97 | 98 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 15 | 15 | kJ/m² | |
| -30°C | 17 | 16 | kJ/m² | |
| 23°C | 21 | 26 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 80 | 75 | kJ/m² | |
| 23°C | 80 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 246 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 75.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 245 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 262 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.5E-5 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.12 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2200 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.22 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Effective Thermal Diffusivity | 0.103 | -- | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3885H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 2800 B-70A Z | RTP Company | TPV | RTP |
| Nanjing Hongrui PP P3010 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| ColorRx® PP2-3500RX | LTL Color Compounders, Inc. | PP Random Copolymer | ColorRx® |
| LNP™ THERMOCOMP™ UC008H compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |