Polifil® ABS RP-ABS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | mfIBxo_Polifil-ABS-RP-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® RP-ABS is a styrenic resin with improved toughness and heat resistance versus HIPS grades. ABS exhibits high gloss, low shrinkage, and good dimensional stability. ABS is widely used in injection molding of appliances, furniture, and automotive parts. ABS also has high melt strength suitable for the production of extruded sheet, some of considerable size and thickness. Applications include panels for large appliances and thermoformed items such as hot tubs and recreational vehicle parts. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.0 to 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2000 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 44.1 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 4.0 | % | |
| Break, 23°C | 20 | % | |
| Flexural Modulus - Tangent (23°C) | 2480 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 190 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | 11.3 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 96.1 | °C | |
| 1.8 MPa, Unannealed | 90.6 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chiao Fu PA6 MC312LST BK | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| KRATON® D0243 K | Kraton Polymers LLC | SBC | KRATON® |
| Lucky Enpla LAY1003E | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |
| Lucent PA NP6-140 | Lucent Polymers, Inc. | Nylon 66 | Lucent PA |
| SQUARE® SSR8630-28AF/BF | Shenzhen SQUARE Silicone Co., Ltd. | Silicone | SQUARE® |