Exelene® LDPE 6001

Category:	LDPE , Low Density Polyethylene
Manufacturer:	Montachem International, Inc.
Trademark:	Exelene® LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	z8T8Ir_Exelene-LDPE-6001.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Applications:

Clothes Covers for Laundromats

Protective bags for bananas in plantations

Characteristics:

The Exelene resin LDPE 6001 meets the requirements of section 177.1520, paragraph C, from chapter 21 denominated "Olefin Polymers" from the Code of Federal Regulations of the FDA, to be utilized with direct food contact.

General Information
Additive	Antiblock Antioxidant Slip
Features	Antiblocking Antioxidant Food Contact Acceptable High Clarity Low Density Slip
Uses	Bags Food Packaging Food Service Applications Laundry Bags Non-specific Food Applications
Agency Ratings	FDA 21 CFR 177.1520(c)
Processing Method	Blown Film Film Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.921	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.0	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Flexural Strength ¹			ASTM D882
-- ²	152	MPa
-- ³	138	MPa

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	38	µm
Tensile Strength ⁴			ASTM D882A
MD : Break	20.7	MPa
TD : Break	15.2	MPa
Tensile Elongation ⁵			ASTM D882A
MD : Break	250	%
TD : Break	600	%
Dart Drop Impact ⁶(38000 µm)	95	g	ASTM D1709A

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	110	°C	DSC

Note Message
1 .	5.1 mm/min
2 .	TD, 1% secant
3 .	MD, 1% secant
4 .	510 mm/min
5 .	510 mm/min
6 .	F50, 66 cm

Resin Grade	Manufacturer	Category	Trademark
CALIBRE™ MEGARAD™ 2081 HD-15 2	Trinseo	PC	CALIBRE™
Cellophane™ CelloPlus™ W (White)	Innovia Films Ltd.	Cellulose, Regenerated	Cellophane™
HI-ZEX™ 5202B	Prime Polymer Co., Ltd.	HDPE	HI-ZEX™
Kumho SBR 1712G	Korea Kumho Petrochemical Co., Ltd.	SBR, Emulsion	Kumho SBR
OnFlex™ S KE 40A-3S1727	PolyOne Corporation	TPE	OnFlex™