Ultramid® A3XZG5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | z0KyGl_Ultramid-A3XZG5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3XZG5 is an impact-modified, 25% glass fiber reinforced injection molding PA66 grade with improved flame retardance. Applications Typical applications include components with high stiffness, dimensional stability and enhanced impact strength such as electrical switches. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6500 | 4500 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 105 | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 6.0 | 11 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 5500 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 25 | 30 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 90 | 100 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| RTI Elec | UL 746 | |||
| 0.750 mm | 120 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 120 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 115 | -- | °C | |
| 1.50 mm | 115 | -- | °C | |
| 3.00 mm | 115 | -- | °C | |
| RTI Str | UL 746 | |||
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C |
| Electrical | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Dielectric Constant (1 MHz) | 3.80 | -- | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.030 | IEC 60250 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | V-0 | -- | ||
| 3.00 mm | V-0 5VA | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 285 to 300 | °C | |
| Middle Temperature | 285 to 300 | °C | |
| Front Temperature | 285 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-A890 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | Wanthane® |
| Fainplast PVC GS 87/BT | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Sylvin 8398-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vyncolit® A2740 | SBHPP | Phenolic | Vyncolit® |
| TechnoElast S D4000 E 2 sw | TechnoCompound GmbH | TPE | TechnoElast |