Daelim Po1y® XP9200E
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | DAELIM INDUSTRIAL CO., LTD. |
| Trademark: | Daelim Po1y® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ekNH7d_DaelimPo1yXP9200E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daelim Po1y®XP9200E is a metallocene linear low density polyethylene product,. It is available in Europe or Asia Pacific. Daelim Po1y®XP9200E application areas include wrapping, film, agriculture, food contact application and coating application. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 56.9 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 45.1 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 580 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 620 | % | ASTM D882 |
| Dart Drop Impact (30 µm, Blown Film) | 700 | g | ASTM D1709B |
| Seal Initiation Temperature 1(30 µm, Blown Film) | 95.0 | °C | Internal method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ASTM D1004 | ||
| Lateral flow : 0.0300mm | 125 | kN/m | ASTM D1004 |
| Traffic : 0.0300mm | 122 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| Peak Melting Temperature | 116 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 30.0 µm, Blown Film) | 87 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Note Message | |
|---|---|
| 1 . | HGT, 2.8 kg, 0.5 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4564 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TPC PVC SG660 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| UBESTA 3024 LU | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Favorite LL565 | Favorite Plastics | LLDPE+EVA | Favorite |
| Plaslube® J-1/CF/10/TF/13/SI/2 NAT | Techmer Engineered Solutions | Nylon 66 | Plaslube® |