EOS PA 2210 FR
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | EOS GmbH |
| Trademark: | EOS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ytP5hZ_EOS-PA-2210-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product information PA 2210 FR is a polyamide 12 for processing in laser sintering systems with a halogen free, chemical flame retardant. In case of fire a carbonating coating arises on the surface of the part, isolating the plastic below. Properties
Acceptance criteria
Typical applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.06 | -- | g/cm³ | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| -- 1 | 2300 | 2200 | MPa | ISO 527-2 |
| -- 2 | 2500 | 2400 | MPa | ISO 527-2 |
| Tensile Stress | ||||
| 3.0% Strain 3 | 41.0 | -- | MPa | ISO 527-2 |
| 4.0% Strain 4 | -- | 38.0 | MPa | ISO 527-2 |
| 4.0% Strain 5 | 46.0 | -- | MPa | ISO 527-2 |
| 6.0% Strain 6 | -- | 43.0 | MPa | ISO 527-2 |
| Tensile Strain | ||||
| Break 7 | 3.0 | 4.0 | % | ISO 527-2 |
| Break 8 | 4.0 | 7.0 | % | ISO 527-2 |
| Flexural Modulus 9(23°C) | 2300 | -- | MPa | ISO 178 |
| Flexural Stress 10 | 65.0 | -- | MPa | ISO 178 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 11 | 185 | -- | °C | ISO 11357 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.10 mm | HB | -- | ||
| 1.20 mm | HB | -- | ||
| 1.30 mm | HB | -- | ||
| 1.40 mm | HB | -- | ||
| 3.00 mm | HB | -- | ||
| 2.00 mm | V-0 | -- | ||
| 2.40 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| 4.00 mm | V-0 | -- | ||
| Flame Test | FAR 25.853 | |||
| 1.70 mm | Passed | -- | ||
| 2.00 mm | Passed | -- | ||
| Smoke Density | AITM 2.0007 | |||
| 1.70 mm | Passed | -- | ||
| 2.00 mm | Passed | -- | ||
| Toxicity | AITM 3.0005 | |||
| 1.70 mm | Passed | -- | ||
| 2.00 mm | Passed | -- |
| Note Message | |
|---|---|
| 1 . | Z Direction |
| 2 . | Y Direction |
| 3 . | Z Direction |
| 4 . | Z Direction |
| 5 . | X Direction |
| 6 . | X Direction |
| 7 . | Z Direction |
| 8 . | Y Direction |
| 9 . | X Direction |
| 10 . | X Direction |
| 11 . | 20°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2599 X 61232 A FR | RTP Company | PC+ABS | RTP |
| RTP 109 Z | RTP Company | PP Homopolymer | RTP |
| Crastin® S600F20 NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Latilub 66-01M G/30 | LATI S.p.A. | Nylon 66 | Latilub |
| Polycomp® PDR CB 08 | PolyPacific Pty. Ltd. | PP Copolymer | Polycomp® |