RX® 865M
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | RX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U4kbuB_RX-865M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RX® 865M is a fiberglass reinforced phenolic novolac compound, featuring dimensional stability, moderate impact resistance, and good strength and modulus. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.88 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.10 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Compression Molded) | 65.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 20000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 135 | MPa | ISO 178 |
| Compressive Stress | 265 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (Compression Molded) | 4.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | > 282 | °C | ISO 75-2/A |
| CLTE | ASTM E831 | ||
| Flow | 1.7E-5 | cm/cm/°C | |
| Transverse | 3.9E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.74 | W/m/K | ASTM C518 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 150 | °C | UL 746 |
| RTI Str | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 14 | kV/mm | ASTM D149 |
| Arc Resistance | 185 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ME-2640DB BLK (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |
| TRANSMARE® BIO 35LA-0.001 | Transmare Compounding B.V. | PLA | TRANSMARE® BIO |
| 3M™ Dyneon™ Fluoroplastic PVDF 31508/0009 | 3M Advanced Materials Division | PVDF | 3M™ Dyneon™ Fluoroplastic |
| Anjacom® 036/80 | Almaak International GmbH | Nylon 6+ASA | Anjacom® |
| Appeel® 20D828 | DuPont Packaging & Industrial Polymers | AEM+TPC-ET | Appeel® |