LNP™ LUBRICOMP™ DFL34 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yQmaWV_LNP-LUBRICOMP-DFL34-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DFL34 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DFL-4034 Product reorder name: DFL34 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.30 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.50 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.11 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.16 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6870 | MPa | ASTM D638 |
| -- | 6510 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 97.0 | MPa | ASTM D638 |
| Yield | 2.90 | MPa | ISO 527-2/5 |
| Yield | 94.0 | MPa | ISO 527-2/50 |
| Break 3 | 95.9 | MPa | ASTM D638 |
| Break | 89.6 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.9 | % | ASTM D638 |
| Yield | 2.9 | % | ISO 527-2/5 |
| Break 5 | 3.3 | % | ASTM D638 |
| Break | 3.5 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4910 | MPa | ASTM D790 |
| -- 7 | 6020 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 143 | MPa | ASTM D790 |
| -- | 153 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 144 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.52 | ||
| vs. Itself - Static | 0.67 | ||
| Wear Factor - Washer | 76.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 9 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 780 | J/m | ASTM D4812 |
| 23°C 10 | 48 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 22.5 | J | ASTM D3763 |
| -- | 7.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 147 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 147 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 143 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 144 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ NEO PG1940 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| NYCOA Polyamide 5033 HST | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| EPLAMID 66 IMP NC A801 | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| Kumho EP HAC 8290NH | Korea Kumho Petrochemical Co., Ltd. | PC+ABS | Kumho EP |
| NORYL™ WCA871A resin | SABIC Innovative Plastics Asia Pacific | PPE | NORYL™ |