Order Products : sales@su-jiao.com
Generic EMA
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | v7haXG_Generic-EMA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic EMA This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.929 - 0.944 | g/cm³ | ASTM D792 |
| 23°C | 0.929 - 0.944 | g/cm³ | ISO 1183 |
| -- | 0.940 - 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 1.6 - 6.6 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.50 - 9.2 | g/10 min | ISO 1133 |
| Methyl Acrylate Content | 17.5 - 24.6 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 21 - 85 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture, 23°C | 5.80 - 12.1 | MPa | ASTM D638 |
| Fracture, 23°C | 6.00 - 13.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 660 - 870 | % | ASTM D638 |
| Fracture, 23°C | 750 - 780 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 8.00 - 85.0 | MPa | ASTM D790 |
| 23°C | 15.7 - 40.7 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -73.4 - -71.9 | °C | ASTM D746 |
| Vicat Softening Temperature | |||
| -- | 42.5 - 61.8 | °C | ASTM D1525 |
| -- | 39.8 - 70.4 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 61.0 - 106 | °C | DSC |
| -- | 74.0 - 96.1 | °C | ASTM D3418 |
| -- | 76.5 - 101 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 - 185 | °C | |
| Cylinder Zone 2 Temp. | 160 - 235 | °C | |
| Cylinder Zone 3 Temp. | 185 - 260 | °C | |
| Cylinder Zone 4 Temp. | 185 - 285 | °C | |
| Cylinder Zone 5 Temp. | 185 - 290 | °C | |
| Adapter Temperature | 185 - 290 | °C | |
| Melt Temperature | 198 - 302 | °C | |
| Die Temperature | 185 - 290 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic EMAThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santron IMS1000M | Bhansali Engineering Polymers Limited | SAN | Santron |
| BESTNYL SE15VI01A | Triesa Plastics | Nylon 66 | BESTNYL |
| Fluoroplex COMP 401 - GMP | UNIFLON | PTFE | Fluoroplex |
| Hostaform® LM25 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| LUVOCOM庐 1105-7107/BK | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
