Durethan® BKV 140 DUS008 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yPlZk4_DurethanBKV140DUS008000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 40 % glass fibers, injection molding, improved impact strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 280°C, 2.00mm 1 | 0.75 | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.090 | % | ISO 2577 |
| Flow direction : 280°C, 2.00mm 3 | 0.21 | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.070 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 185 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.4 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 11000 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% strain, 23°C | 280 | MPa | ISO 178/A |
| 23°C 6 | 290 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 4.2 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA 6HI, GR, 14-120, GF40 | ISO 1874 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 100 | kJ/m² | ISO 179/1eU |
| 23°C | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 90 | kJ/m² | ISO 180/1U |
| 23°C | 90 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 217 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 201 | °C | ISO 75-2/A |
| Melting Temperature 8 | 220 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 260 - 290 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 400 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 400 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEETEC PP H1615 | LG Chem Ltd. | PP Homopolymer | SEETEC PP |
| NYLAFORCE® A 60 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | NYLAFORCE® |
| Ferro PP NPP00GX03WH | Ferro Corporation | PP Copolymer | Ferro PP |
| Plaslube® PA6/6 8111 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Sylvin 6200-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |