Plexiglas® Satinice df33 7H
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Evonik Industries AG |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yIsynV_Plexiglas-Satinice-df33-7H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PLEXIGLAS® Satinice df33 7H, based on PLEXIGLAS® 7H, is characterized by diffuse scattering of light. Typical properties of impact modified PLEXIGLAS® molding compound are
Extruded parts from PLEXIGLAS® Satinice df33 7H are characterized by the following special properties:
Application: Used for (Co-) extruding profiles and sheets for the construction, furniture and automotive industry. Examples: applications that call for light diffusion combined with optimum transmission and velvet matt surface appearance is desired. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/3.8 kg) | 0.900 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 99.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 102 | °C | ISO 306/B50 |
| CLTE - Flow (0 to 50°C) | 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 700 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 1 | ISO 2813 | ||
| 105° | 16 | ||
| 90° | 9 | ||
| Transmittance 2(3000 µm) | 69.0 | % | ISO 13468-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Half-Value Angle | 34.0 | ° | DIN 5036 |
| Scattering Power | 0.470 | DIN 5036 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Melt Temperature | 230 to 260 | °C | |
| Die Temperature | 230 to 260 | °C |
| Note Message | |
|---|---|
| 1 . | R60, f(polishing roll temperatur) |
| 2 . | D65 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMAPET® N180 | Indorama Ventures PCL | PET | RAMAPET® |
| SCHULAMID® 6 GF 20 H LS | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Shinko-Lac® ABS HF-5 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| LEXAN™ LC120 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Padermid 6 AF-S | TKC Kunststoffe e.K. | Nylon 6 | Padermid |