Santoprene™ 8201-90

Category: TPV , Thermoplastic Vulcanizate
Manufacturer: ExxonMobil Chemical
Trademark: Santoprene™
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: yI1nLl_Santoprene-8201-90.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
It is a hard, colorable, non-hygroscopic thermoplastic vulcanized elastomer (TPV) in the thermoplastic elastomer (TPE) series. This material has good physical properties and chemical resistance at the same time, and is suitable for a wide range of fields. This brand of Shanduping TPV is a shear rate dependent product that can be processed on conventional thermoplastic injection molding, extrusion molding, blow molding, thermoforming or vacuum forming equipment. This is a polyolefin-based material that can be recycled in the production process.
General Information
Features
  • Low friction coefficient
  • Lower die-out expansion
  • Recyclable materials
  • Controllable die-out expansion
  • Cleanable
  • Good melt strength
  • Good coloring
  • Ozone resistance
  • Good chemical resistance
  • Low or no water absorption
Uses
  • Kitchen utensils
  • Home appliance components
  • Fatigue elimination supplies
  • Soft handle
  • Mobile phone
  • Stationery
Agency Ratings
  • UL QMFZ2
  • UL QMFZ8
RoHS Compliance
  • RoHS compliance
UL File Number
  • E80017
Appearance
  • Natural color
Forms
  • Particle
Processing Method
  • Blow molding
  • Multiple injection molding
  • Co-extrusion molding
  • Extrusion
  • Extrusion blow molding
  • Sheet extrusion molding
  • Thermoforming
  • Profile extrusion molding
  • Vacuum forming
  • Injection blowing molding
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity
    -- 0.938g/cm³ASTM D792
    -- 0.940g/cm³ISO 1183
HardnessNominal ValueUnitTest Method
Durometer Hardness (Shaw A, 15 seconds, 23°C, 2.00mm)94ISO 868
ElastomersNominal ValueUnitTest Method
Tensile Stress - Across Flow (100% Strain, 23°C)7.10MPaASTM D412, ISO 37
Tensile Strength - Across Flow (Break, 23°C)13.0MPaASTM D412, ISO 37
Tensile Elongation - Across Flow (Break, 23°C)620%ASTM D412, ISO 37
Tear Strength - Across Flow
    23°C 148.0kN/mASTM D624
    23°C 248kN/mISO 34-1
Compression Set
    70°C, 22 hr 352%ASTM D395B
    70°C, 22 hr 452%ISO 815
AgingNominal ValueUnitTest Method
Change in Tensile Strength in Air (150°C, 168 hr)1.0%ASTM D573, ISO 188
Change in Ultimate Elongation in Air (150°C, 168 hr)-15%ASTM D573, ISO 188
Change in Durometer Hardness in Air (Shore A, 150°C, 168 hr)1.0ASTM D573, ISO 188
Change in Mass in Air (150°C, 168 hr)-7.0%ASTM D573
Change in Mass in Air (150°C, 168 hr)-7.0%ISO 188
Change in Tensile Strength ASTM D471, ISO 1817
    23°C, 168 hr, in 15% sodium chloride -1.0%ASTM D471, ISO 1817
    23°C, 168 hr, in 50% sodium hydroxide -2.0%ASTM D471, ISO 1817
    23°C, 168 hr, in 98% sulfuric acid 4.0%ASTM D471, ISO 1817
    23°C, 168 hr, in IRM 903 oil -9.0%ASTM D471, ISO 1817
    23°C, 168 hr, in water 1.0%ASTM D471, ISO 1817
Change in Ultimate Elongation ASTM D471, ISO 1817
    23°C, 168 hr, in 15% sodium chloride -2.0%ASTM D471, ISO 1817
    23°C, 168 hr, in 50% sodium hydroxide 0.0%ASTM D471, ISO 1817
    23°C, 168 hr, in 98% sulfuric acid 6.0%ASTM D471, ISO 1817
    23°C, 168 hr, in IRM 903 oil 2.0%ASTM D471, ISO 1817
    23°C, 168 hr, in water 17%ASTM D471, ISO 1817
Change in Durometer Hardness
    Support A, 23°C, 168 hr, in 15% sodium chloride 0.0ASTM D471
    Support A, 23°C, 168 hr, in 50% sodium hydroxide 0.0ASTM D471
    Support A, 23°C, 168 hr, in 98% sulfuric acid 2.0ASTM D471
    Support A, 23°C, 168 hr, in IRM 903 oil -5.0ASTM D471
    Support A, 23°C, 168 hr, in water -1.0ASTM D471, ISO 1817
    Support A, 23°C, 168 hr, in 15% sodium chloride 0.0ISO 1817
    Support A, 23°C, 168 hr, in 50% sodium hydroxide 0.0ISO 1817
    Support A, 23°C, 168 hr, in 98% sulfuric acid 2.0ISO 1817
    Support A, 23°C, 168 hr, in IRM 903 oil -5.0ISO 1817
Change in Mass ASTM D471
    23°C, 168 hr, in 15% sodium chloride 1.0%ASTM D471
    23°C, 168 hr, in 50% sodium hydroxide 2.0%ASTM D471
    23°C, 168 hr, in 98% sulfuric acid 1.0%ASTM D471
    23°C, 168 hr, in IRM 903 oil 18%ASTM D471
    23°C, 168 hr, in water -2.0%ASTM D471
Change in Mass ISO 1817
    23.0°C, 168 hr, in water -2.0%ISO 1817
    23.0°C, 168 hr, in 98% sulfuric acid 1.0%ISO 1817
    23.0°C, 168 hr, in 15% sodium chloride 1.0%ISO 1817
    23.0°C, 168 hr, in 50% sodium hydroxide 2.0%ISO 1817
    23.0°C, 168 hr, in IRM 903 oil 18%ISO 1817
ThermalNominal ValueUnitTest Method
Brittleness Temperature -54.0°CASTM D746, ISO 812
RTI Elec 100°CUL 746
RTI UL 746
    1.10 mm 90.0°CUL 746
    1.60 mm 95.0°CUL 746
    3.00 mm 95.0°CUL 746
ElectricalNominal ValueTest Method
Comparative Tracking Index (CTI) PLC 0UL 746
High Amp Arc Ignition (HAI) PLC 0UL 746
High Voltage Arc Resistance to Ignition (HVAR) PLC 5UL 746
Hot-wire Ignition (HWI) UL 746
    1.60 mm PLC 3UL 746
    3.00 mm PLC 2UL 746
FlammabilityNominal ValueTest Method
Flame Rating UL 94
    1.10 mm HBUL 94
    1.60 mm HBUL 94
    3.00 mm HBUL 94
Additional Information
如果适用，这是基于扇形浇口注塑成型的平板测试结果。拉伸强度、伸长率和拉伸应力沿垂直流动方向测定 - ISO 1 型，ASTM die C。25% 形变时的永久压缩变形。从埃克森美孚欧洲分支机构直接购买的所有产品都符合 REACH 法规。 对于埃克森 美孚未进口至欧洲的产品，用户应自行评估其是否满足 REACH 法规。
Legal statement
未经埃克森美孚化工书面允许，这种产品包括其产品名称，不得在任何医疗应用领域予以使用或有关详细的产品监管信息，请联系客户服务。
InjectionNominal ValueUnit
Suggested Max Moisture 0.080%
Suggested Max Regrind 20%
Rear Temperature 191 - 204°C
Middle Temperature 196 - 210°C
Front Temperature 196 - 210°C
Nozzle Temperature 210 - 221°C
Processing (Melt) Temp 199 - 216°C
Mold Temperature 23.9 - 51.7°C
Injection Rate Fast
Back Pressure 0.345 - 0.689MPa
Screw Speed 100 - 200rpm
Clamp Tonnage 4.1 - 6.9kN/cm²
Cushion 3.18 - 6.35mm
Screw L/D Ratio 16.0:1.0 to 20.0:1.0
Screw Compression Ratio 2.0:1.0 to 2.5:1.0
Vent Depth 0.025mm
Injection instructions
Santoprene TPV与乙缩醛和PVC不相容。更多关于加工和模具设计的信息，请查阅我们的《注射成型指南》。
ExtrusionNominal ValueUnit
Melt Temperature 196 - 224°C
Die Temperature 196 - 224°C
Extrusion instructions
Santoprene TPV与乙缩醛和PVC不相容。更多关于加工和模具设计的信息，请查阅我们的《挤出成型指南》。
Note Message
1 .C mould
2 .Method B, right-angle specimen (cut)
3 .Type 1
4 .Type a
Resin Grade Manufacturer Category Trademark
TARFLON™ #2200 Formosa Idemitsu Petrochemical Corporation PC TARFLON™
BMC T40(18)-LS Bulk Molding Compounds, Inc. Polyester, TS BMC
Fainplast PVC GS 75/O Fainplast Compounds S.r.l PVC, Unspecified Fainplast PVC
Geon™ HC 2160G PolyOne Corporation PVC, Flexible Geon™ HC
OTECH ALLOY OTO9275 - Riser Jacket OTECH Corporation TP, Unspecified OTECH ALLOY

TEL: +86-21-58958519 Email:sales@su-jiao.com

No. 215, Lianhe North Road, Fengxian District, Shanghai, China​， COPYRIGHT SUSHENG COMPANY RIGHTS RESERVED