VESTAMID® D X7099
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® D |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | yCRumR_VESTAMID-D-X7099.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characterization: 20% glass fiber reinforced, heat-stabilized Applications: housings, sealing and damping elements for the automotive industry, noise and vibration-damping sliding bearings and rollers Its advantages over PA 12 exhibit in the
The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.20 | 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.60 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 2.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5600 | -- | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 118 | -- | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 5.0 | -- | % | ISO 527-2/1A |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C, Complete Break | 7.0 | -- | kJ/m² | |
| 23°C, Complete Break | 10 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C, Complete Break | 60 | -- | kJ/m² | |
| 23°C, Complete Break | 80 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 210 | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 190 | 190 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | 205 | °C | ISO 306/B |
| Melting Temperature 2 | 215 | 215 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 5.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 38 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.40 | -- | ||
| 1 MHz | 3.90 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.065 | -- | ||
| 1 MHz | 0.043 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | HB | ||
| 3.20 mm | HB | -- |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA612, MH, 14-050, GF20 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | specimen 127x12.7x3.2 mm processing acc. to ISO 1874-2 |
| 2 . | 2nd Heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MIDILENA III PPJ1000 | ROMPETROL PETROCHEMICALS S.R.L. | PP Homopolymer | MIDILENA III |
| SURPASS® RMs539-U(UG) | NOVA Chemicals | LLDPE | SURPASS® |
| Nypol® PA A3 PRTA010 NR326 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Geon™ Vinyl Flexible 90051 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 9466-50D Natural | Sylvin Technologies Incorporated | PVC+PUR | Sylvin |