LEXAN™ LUX2719 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xsuvRX_LEXAN-LUX2719-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lexan* LUX2719 Polycarbonate resin is an extrusion grade. It is UL94 V-2 rated at 1.5 mm. It was designed for high light reflectance. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.31 | g/cm³ | ASTM D792 |
| -- | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.80 to 1.0 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 59.0 | MPa | |
| Break | 56.0 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 100 | % | |
| Flexural Modulus 3(50.0 mm Span) | 2550 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 500 | J/m | |
| 23°C | 700 | J/m | |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 63.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 142 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 129 | °C | |
| Vicat Softening Temperature | 147 | °C | ASTM D1525 5 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 6.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.4E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.00 to 3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 825 | °C | |
| 3.00 mm | 825 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 288 to 310 | °C | |
| Middle Temperature | 299 to 321 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 304 to 327 | °C | |
| Processing (Melt) Temp | 310 to 332 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sicoklar E01.04 | Ravago Group | PC | Sicoklar |
| VINIKA® CF80AC | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Celanex® XFR 6842 GF15 | Celanese Corporation | PBT | Celanex® |
| Chiao Fu PA6 MC312G45 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| Petrotene® PP A3 C35 BRC0001 PH333 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |