WPP PP PRC25TF2HFL-Black
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | pzo8hy_WPP-PP-PRC25TF2HFL-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PRC25TF2HFL-Black is a polypropylene homopolymer (PP Homopoly) product, which contains 20% talc filler. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 31.0 | MPa | ASTM D638 |
| Yield | 29.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 2 | 20 | % | ASTM D638 |
| Fracture | 10 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 6.00 mm 3 | 2600 | MPa | ASTM D790 |
| -- 4 | 2200 | MPa | ISO 178 |
| Flexural Strength 5(6.00 mm) | 48.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| -10°C, 6.00 mm | 21 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 32 | J/m | ASTM D256 |
| -40°C | 2.0 | kJ/m² | ISO 180 |
| -10°C | 2.4 | kJ/m² | ISO 180 |
| 23°C | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.00mm | 140 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 73.0 | °C | ISO 75-2/A |
| 1.8 MPa, not annealed | 71.0 | °C | ISO 75-2/Af |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 30 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 30 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5415 | Spartech Polycom | PP, Unspecified | Spartech |
| Moplen EP 3307 | LyondellBasell Industries | PP Copolymer | Moplen |
| Kumho EP HAC 8250NH | Korea Kumho Petrochemical Co., Ltd. | PC+ABS | Kumho EP |
| Polyclear® Crystal PET 3302 | Auriga Polymers Inc. | PET | Polyclear® |
| Ultramid® B27 12 | BASF Corporation | Nylon 6 | Ultramid® |