ColorFast® PP1-FRV2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LTL Color Compounders, Inc. |
| Trademark: | ColorFast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xkK4HQ_ColorFast-PP1-FRV2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| V-2 rated ?ame retardard extrusion grade PP |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 to 20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.010 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1450 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 90 | % | ASTM D638 |
| Flexural Modulus 4 | 1280 | MPa | ASTM D790 |
| Flexural Strength 5 | 37.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 32 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 51.7 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 48.9 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 182 to 204 | °C | |
| Middle Temperature | 188 to 210 | °C | |
| Front Temperature | 193 to 216 | °C | |
| Nozzle Temperature | 199 to 227 | °C | |
| Processing (Melt) Temp | 199 to 227 | °C | |
| Mold Temperature | 10.0 to 37.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| 5 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ FFX125 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| Medalist® MD-12342 | Teknor Apex Company | TPE | Medalist® |
| Akulon® K222-KGV5 | DSM Engineering Plastics | Nylon 6 | Akulon® |
| MAJORIS HG313X - 8147 | AD majoris | PP, Unspecified | MAJORIS |
| INNATE™ ST50 Precision Packaging Resin | The Dow Chemical Company | PE, Unspecified | INNATE™ |