Order Products : sales@su-jiao.com
AVP™ GYYHSUVCP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rYgUYI_AVP-GYYHSUVCP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVP™ GYYHSUVCP is a Polyamide 66 (Nylon 66) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.3 to 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Ultimate, 3.18 mm) | 79.3 | MPa | ASTM D638 |
| Flexural Modulus 2(3.18 mm, 50.8 mm Span) | 2480 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 43 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 76.7 | °C | ASTM D648 |
| Melting Temperature | 249 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 249 to 282 | °C | |
| Middle Temperature | 260 to 288 | °C | |
| Front Temperature | 271 to 304 | °C | |
| Nozzle Temperature | 271 to 304 | °C | |
| Processing (Melt) Temp | 271 to 304 | °C | |
| Mold Temperature | 65.6 to 110 | °C | |
| Back Pressure | 0.172 to 1.03 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Ofluorine PVDF 9202 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| Caltex PP MT64WS | GS Caltex | PP, Unspecified | Caltex PP |
| Hostacom TRC 152N KF | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Karina BLACK PVC COMPOUND 834-48/ 1-A-ERM-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| HIPOLEN P® MA 71 | Hipol a.d. | PP Homopolymer | HIPOLEN P® |