China PPS PTFE-hCF313
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | xchcSv_China-PPS-PTFE-hCF313.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS/PTFE-hCF313 is lubricant PPS compound, which is filled with carbon fiber, PTFE and ingredients based on the PPS resin. It shows solvent resistance, abrasion resistance and good mechanic prosperity, high modulus, creep resistance, high-temperature resistance, inherent flame resistance, easy processing, low mold shrinkage, good dimensional stability. Owing to its high performance, it's an excellent selection for making high performance structures and wearing pieces with high wear resistance, high temperature resistance, high pressure resistance and high corrosion resistance; axle sleeve in high rotating condition; high modulus wear resistant parts in aero industry and weapon industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | Internal method |
| Molding Shrinkage - Flow | 0.25 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness 1 | 104 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 161 | MPa | Internal method |
| Tensile Elongation (Break) | 1.8 | % | Internal method |
| Flexural Modulus | 16900 | MPa | Internal method |
| Flexural Strength | 243 | MPa | Internal method |
| Coefficient of Friction | 0.17 | Internal method | |
| Abrasion - Width | 6 | mm | Internal method |
| Abrasion Loss 2 | 4.5 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 12 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 263 | °C | Internal method |
| Melting Temperature | 281 | °C | Internal method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 2 to 8hr |
| Note Message | |
|---|---|
| 1 . | HR |
| 2 . | 120 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ PEEK KD2000-J01 | Polymics, Ltd. | PEEK | Pyramid™ PEEK |
| DOW™ LDPE 959S | The Dow Chemical Company | LDPE | DOW™ LDPE |
| BCC Resins BC 8005 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| Andur AL 80-5 AP/Curene® 110 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| OTECH PVC OE8739 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |