Pyramid™ PEEK KD2000-J01
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Pyramid™ PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KdUUEg_Pyramid-PEEK-KD2000-J01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyetheretherketone, Unfilled, Standard Flow |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | < 0.20 | % | ASTM D570 |
| Crystallinity | < 30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ASTM D638 |
| Tensile Strength (Break) | 97.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 40 | % | ASTM D638 |
| Flexural Modulus | 3500 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 159 | MPa | ASTM D790 |
| Compressive Strength | 131 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Glass Transition Temperature | 143 | °C | ASTM D3418 |
| Melting Temperature | 339 | °C | DSC |
| CLTE - Flow | 4.7E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | 3.30 | ASTM D150 | |
| Dissipation Factor | 4.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y3700C (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Hyundai EP PA66 LD340 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| SHINSTRA WG30F | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |
| Kepamid® 2333GB | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |
| apilon 52® FA-56E | API SpA | TPU-Polyester | apilon 52® |